Orange Abrasion-resistant SBR Skirting Rubber Gasket
- Meets ASTM D 2000 M2 AA510A13B13C12G21J1
- Ideal for skirting Rubber Liners
- Conveyor Skirting 50° Shore
- View material – Coru1321-20-14
Call for Price
You save (%)
|
Properties |
Test Method |
Values |
Test Method |
Values |
|
|
|
FPS Units |
|
Metric Units |
|
Specific Gravity |
DIN 53508 |
1.20±0.05 |
ASTM D297 |
1.20±0.05 |
|
Hardness |
DIN 53505 |
50 ± 5 Sh A |
ASTM D2240 |
50 ± 5 Sh A |
|
Tensile Strength (min) |
DIN 53504 |
1140 PSI |
ASTM D412 |
80 kg/cm2 |
|
Elongation at Break (min) |
DIN 53504 |
300% |
ASTM D412 |
300% |
|
Abrasion Resistance (max) |
DIN 53516 |
140 mm3 |
ASTM D5963 |
140 mm3 |
|
Compression Set (70ºC/24 hrs./25% compression) (max) |
DIN 53517 |
40% |
ASTM D395 METHOD B |
40% |
|
Tear Resistance (Angular) min |
DIN 53515 |
123 Lbs/Inch |
ASTM D624 |
22 Kg/cm |
|
Change in Properties After |
|
|
|
|
|
Heat Ageing For (72 hrs. AT 70 ºC) |
|
|
ASTM D573 |
|
|
— Hardness (Pts) |
|
+ 5 (Max) |
|
+ 5 (Max) |
|
— Tensile Strength (%) |
|
+ 10 / -25 |
|
+ 10 / -25 |
|
— Elongation at Break (%) |
|
+ 10 / -25 |
|
+ 10 / -25 |
|
Volume Swell: at 70ºC for 72 hrs |
|
|
ASTM D 471 |
|
|
In IRM Oil No.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
In IRM Oil No.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
In IRM Oil No.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
Chemical Resistance |
|
|
|
|
|
— Ozone |
|
FAIR |
ASTM D 1149 |
FAIR |
|
— Dilute Acids and Bases |
|
GOOD |
|
GOOD |
|
— Concentrated Acids and Bases |
|
FAIR |
|
FAIR |
|
— Oils |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— Solvents |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
Temperature Range |
|
-30º to + 70 ºC |
|
-30º to + 70 ºC |
|
Colour |
|
BLACK |
|
BLACK |
|
Properties |
Test Method |
Values |
Test Method |
Values |
|
|
|
FPS Units |
|
Metric Units |
|
Specific Gravity |
DIN 53508 |
1.20±0.05 |
ASTM D297 |
1.20±0.05 |
|
Hardness |
DIN 53505 |
50 ± 5 Sh A |
ASTM D2240 |
50 ± 5 Sh A |
|
Tensile Strength (min) |
DIN 53504 |
1140 PSI |
ASTM D412 |
80 kg/cm2 |
|
Elongation at Break (min) |
DIN 53504 |
300% |
ASTM D412 |
300% |
|
Abrasion Resistance (max) |
DIN 53516 |
140 mm3 |
ASTM D5963 |
140 mm3 |
|
Compression Set (70ºC/24 hrs./25% compression) (max) |
DIN 53517 |
40% |
ASTM D395 METHOD B |
40% |
|
Tear Resistance (Angular) min |
DIN 53515 |
123 Lbs/Inch |
ASTM D624 |
22 Kg/cm |
|
Change in Properties After |
|
|
|
|
|
Heat Ageing For (72 hrs. AT 70 ºC) |
|
|
ASTM D573 |
|
|
— Hardness (Pts) |
|
+ 5 (Max) |
|
+ 5 (Max) |
|
— Tensile Strength (%) |
|
+ 10 / -25 |
|
+ 10 / -25 |
|
— Elongation at Break (%) |
|
+ 10 / -25 |
|
+ 10 / -25 |
|
Volume Swell: at 70ºC for 72 hrs |
|
|
ASTM D 471 |
|
|
In IRM Oil No.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
In IRM Oil No.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
In IRM Oil No.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
Chemical Resistance |
|
|
|
|
|
— Ozone |
|
FAIR |
ASTM D 1149 |
FAIR |
|
— Dilute Acids and Bases |
|
GOOD |
|
GOOD |
|
— Concentrated Acids and Bases |
|
FAIR |
|
FAIR |
|
— Oils |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— Solvents |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
Temperature Range |
|
-30º to + 70 ºC |
|
-30º to + 70 ºC |
|
Colour |
|
BLACK |
|
BLACK |