White Silicone WRAS Grade 60° shore
- Excellent concentrated and diluted acid resistance
- Very good aging and weathering characteristics
- Suitable for use with food and drink with WRAS approval
- Reach, RoHS, PAH, and CE compliant
Call for Price
You save (%)
This product is available for bespoke manufacturing, please choose an option below:
SM14105 White Silicone WRAS Grade 60° shore is high quality sheeting for demanding applications with excellent concentrated and diluted acid resistance together with very good aging and weathering characteristics and suitable for use with food and drink.
N.B. Coruba Sheeting can be supplied plain or with self-adhesive backed tape (SAB). Rubber Strip to bespoke sizes are available along with customised sheets/gaskets. Please email your enquiry details to sales@coruba.co.uk.
Complies to US FDA 21 CFR177.2600. & EU 1935/2004 and USP Class VI Compliant
WRAS APPROVAL NUMBER: 1302541
This Product is REACH, RoHS, PAH and CE Compliant.
- Material Profile: See Below
- Thickness: 1mm-6mm
- Sheet Size: 1.2m wide in 10m rolls
- Finish: Smooth finish
- Cutting: Standard press-tools
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.20±0.05 |
ASTM D297 |
1.20±0.05 |
|
HARDNESS |
DIN 53505 |
60 ± 5 |
ASTM D2240 |
60 ± 5 |
|
TENSILE STRENGTH (KG/CM2) |
DIN 53504 |
712 PSI |
ASTM D412 |
60 KG/CM2 |
|
ELONGATION AT BREAK % ( MIN ) |
DIN 53504 |
250 |
ASTM D412 |
250 |
|
COMPRESSION SET (150º C/24 HRS/25% SET) (MAX) |
DIN ISO 815-1 |
40% |
ASTM D395 METHOD B |
40% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
112 LBS/INCH |
ASTM D624 |
20 KG/CM |
|
POLYMER CONTENT (%) |
100% |
100% |
||
|
CHANGE IN PROPERTIES |
||||
|
HEAT AGEING ( 72 HRS. AT 100 ºC ) |
ASTM D573 |
|||
|
— HARDNESS (PTS) |
3 |
3 |
||
|
— TENSILE STRENGTH (%) |
±5 |
±5 |
||
|
— ELONGATION AT BREAK (%) |
±5 |
±5 |
||
|
WRAS QUALITY TEST |
APPROVED |
BS 6920 : PART 3 : 2000 |
APPROVED |
|
| VOLUME SWELL: AT 70º C FOR 72 HRS/IN |
ASTM D 471 |
|||
|
OZONE (20% STRETCH 40°C FOR 72 HRS AT 50 PPHM) |
EXCELLENT |
ASTM D 1149 |
EXCELLENT |
|
|
— DILUTE ACIDS AND BASES |
EXCELLENT |
EXCELLENT |
||
|
— CONCENTRATED ACIDS AND BASES |
EXCELLENT |
EXCELLENT |
||
|
TEMPERATURE RANGE |
-50 to 200°C |
-50 to 200°C |
||
|
COLOUR |
WHITE |
WHITE |
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.20±0.05 |
ASTM D297 |
1.20±0.05 |
|
HARDNESS |
DIN 53505 |
60 ± 5 |
ASTM D2240 |
60 ± 5 |
|
TENSILE STRENGTH (KG/CM2) |
DIN 53504 |
712 PSI |
ASTM D412 |
60 KG/CM2 |
|
ELONGATION AT BREAK % ( MIN ) |
DIN 53504 |
250 |
ASTM D412 |
250 |
|
COMPRESSION SET (150º C/24 HRS/25% SET) (MAX) |
DIN ISO 815-1 |
40% |
ASTM D395 METHOD B |
40% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
112 LBS/INCH |
ASTM D624 |
20 KG/CM |
|
POLYMER CONTENT (%) |
100% |
100% |
||
|
CHANGE IN PROPERTIES |
||||
|
HEAT AGEING ( 72 HRS. AT 100 ºC ) |
ASTM D573 |
|||
|
— HARDNESS (PTS) |
3 |
3 |
||
|
— TENSILE STRENGTH (%) |
±5 |
±5 |
||
|
— ELONGATION AT BREAK (%) |
±5 |
±5 |
||
|
WRAS QUALITY TEST |
APPROVED |
BS 6920 : PART 3 : 2000 |
APPROVED |
|
| VOLUME SWELL: AT 70º C FOR 72 HRS/IN |
ASTM D 471 |
|||
|
OZONE (20% STRETCH 40°C FOR 72 HRS AT 50 PPHM) |
EXCELLENT |
ASTM D 1149 |
EXCELLENT |
|
|
— DILUTE ACIDS AND BASES |
EXCELLENT |
EXCELLENT |
||
|
— CONCENTRATED ACIDS AND BASES |
EXCELLENT |
EXCELLENT |
||
|
TEMPERATURE RANGE |
-50 to 200°C |
-50 to 200°C |
||
|
COLOUR |
WHITE |
WHITE |