White Natural Rubber to BS1154 Y50
- REACH, RoHS, PAH and CE compliant
- Commonly requested by Government bodies, Military and Construction organisations
- Used for high performance applications where high tensile and abrasions requirements are important
- Tested to BS1154
- High Quality Natural Rubber: 50° Shore
From £68.90 Excl. VAT
You save (%)
This product is available for bespoke manufacturing, please choose an option below:
Coru222 Off-White Natural Rubber to BS1154 Y50 is a high quality natural rubber grade fully tested to British Standard BS1154 in White for high performance applications where high tensile and abrasion requirements are important. Commonly requested by government bodies, military and construction organisations.
N.B. Available in plain or self-adhesive backed tape (SAB) alternatives. Bespoke sheets and gaskets are available, as well as customised rubber strips. Email your enquiries to sales@coruba.co.uk.
Material Profile (see below):
- Thickness: 3mm to 6mm (other thickness’ on request)
- Sheet Size: 1.4m wide in 10m rolls
- Finish: Smooth finish
- Cutting: Standard press-tools
Other grades, colours and finishes are available – subject to minimum batch quantities.
|
PROPERTIES |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
BS 903: PART A1 |
1.15 |
|
HARDNESS |
BS 903: PART A26 |
50 ± 5 IRHD |
|
TENSILE STRENGTH (KG/CM2) |
BS 903: PART A2 |
170 |
|
ELONGATION AT BREAK ( MIN ) |
BS 903: PART A2 |
500% |
|
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) |
BS 903: PART A6 |
30% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
BS 903: PART A3 |
35 KG/CM |
|
ABRASION RESISTANCE |
|
125mm3 |
|
CHANGE IN PROPERTIES |
|
|
|
HEAT AGEING (168 HRS. AT 70ºC ) |
BS 903: PART A 19 |
|
|
— HARDNESS (PTS) |
BS 903: PART A26 |
+ 5 / -5 (MAX) |
|
— TENSILE STRENGTH (%) |
BS 903: PART A2 |
-10 (MAX) |
|
— ELONGATION AT BREAK (%) |
BS 903: PART A2 |
-15(MAX) |
|
POLYMER CONTENT (NATURAL RUBBER) |
|
100% |
|
ADDITIONAL INFORMATION – |
|
|
|
CHEMICAL RESISTANCE |
|
|
|
— OZONE |
BS 903: PART A43 |
GOOD |
|
— DILUTE ACIDS AND BASES |
BS 903: PART A16 |
FAIR |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-20º TO + 70ºC |
|
COLOUR |
|
OFF-WHITE |
|
PROPERTIES |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
BS 903: PART A1 |
1.15 |
|
HARDNESS |
BS 903: PART A26 |
50 ± 5 IRHD |
|
TENSILE STRENGTH (KG/CM2) |
BS 903: PART A2 |
170 |
|
ELONGATION AT BREAK ( MIN ) |
BS 903: PART A2 |
500% |
|
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) |
BS 903: PART A6 |
30% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
BS 903: PART A3 |
35 KG/CM |
|
ABRASION RESISTANCE |
|
125mm3 |
|
CHANGE IN PROPERTIES |
|
|
|
HEAT AGEING (168 HRS. AT 70ºC ) |
BS 903: PART A 19 |
|
|
— HARDNESS (PTS) |
BS 903: PART A26 |
+ 5 / -5 (MAX) |
|
— TENSILE STRENGTH (%) |
BS 903: PART A2 |
-10 (MAX) |
|
— ELONGATION AT BREAK (%) |
BS 903: PART A2 |
-15(MAX) |
|
POLYMER CONTENT (NATURAL RUBBER) |
|
100% |
|
ADDITIONAL INFORMATION – |
|
|
|
CHEMICAL RESISTANCE |
|
|
|
— OZONE |
BS 903: PART A43 |
GOOD |
|
— DILUTE ACIDS AND BASES |
BS 903: PART A16 |
FAIR |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-20º TO + 70ºC |
|
COLOUR |
|
OFF-WHITE |