Free delivery on orders over £1200.00, all other orders have a fixed rate of £20.00 + VAT.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
Please note: All cut material is non-returnable unless faulty as these are non-sellable and have been cut to specific requirements.
White Food Quality FDA Approved Neoprene Gasket
SKU: GSKT-Coru162
- Approved to: US FDA21 CFR177,2600,EU1935/2004
- USP Class V1 Compliant
- Food Quality Neoprene: 65° Shore
- White – RAL 1015
- View material – Coru162
Call for Price
You save (%)
Chemical Resistances
Acetic Acid, Brine, Calcium Chloride, Carbon Dioxide, Carbon Monoxide, Carbonic Acid, Castor Oil, Sodium Hydroxide, Citric Acid, Corn Oil, Crude Oil, Diesel Oil, Fatty Acids, Formaldehyde, Glucose, Grease, Hydrogen Gas, Hydrogen Sulphide, Lard, Lime, Linoleic Acid, Linseed Oil, Lubricating Oils, Mineral Oil, Neon Gas, Nitrogen, Oil Petroleum, Oleic Acid, Paraffin Wax, Petroleum Oils, Phosphoric Acid, Pine Oil, Potassium Carbonate, Sea Water, Sewage, Sodium Peroxide, Steam, Sulfuric Acid, Toluene, Transformer Oil, Urea, Varnish, Vegetable Oil, Vinegar
Technical Information
| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | DIN 53508 | 1.60 ± 0.05 | ASTM D297 | 1.60 ± 0.05 |
| HARDNESS | DIN 53505 | 65 ± 5 SH A | ASTM D2240 | 65 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | DIN 53504 | 716 PSI | ASTM D412 | 50 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | DIN 53504 | 250 | ASTM D412 | 250 |
| COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) | DIN ISO 815-1 | 30 | ASTM D395 METHOD B | 30 |
| TEAR RESISTANCE ( ANGULAR ) MIN | DIN 53515 | 196 LBS/INCH | ASTM D624 | 35 KG/CM |
| CHANGE IN PROPERTIES | ||||
| HEAT AGEING ( 72 HRS. AT 70 ºC ) | ASTM D573 | |||
| — HARDNESS (PTS) | + 5 (MAX) | + 5 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / – 15 | + 10 / – 15 | ||
| — ELONGATION AT BREAK (%) | + 10 / – 20 | + 10 / – 20 | ||
| VOLUME SWELL : AT 70º C FOR 72 HRS/IN | ASTM D 471 | |||
| IRM OIL NO.1 | + 2 % | + 2 % | ||
| IRM OIL NO.2 | + 15% | + 15% | ||
| IRM OIL NO.3 | + 45% | + 45% | ||
| POLYMER CONTENT (NEOPRENE) | 100% | 100% | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | FAIR | ASTM D 1149 | FAIR | |
| — DILUTE ACIDS AND BASES | GOOD | GOOD | ||
| — CONCENTRATED ACIDS AND BASES | FAIR | FAIR | ||
| — OILS | GOOD | GOOD | ||
| — SOLVENTS | FAIR | FAIR | ||
| TEMPERATURE RANGE | -30º TO + 130º C | -30º TO + 130º C | ||
| COLOUR | WHITE – RAL 1015 | |||
| EXTRACTANTS | TEST CONDITION | AMOUNT OF EXTRACTIVES (MG/INCH²) 1 | ACCEPTABLE LIMIT (MG/INCH²) | CONCLUSION |
| DISTILLED WATER | AT REFLUX TEMP’ FOR 7 HOURS | <0.1 | <20 | PASS |
| DISTILLER WATER | AT REFLUX TEMP FOR SUCCEEDING 2 HOURS OF EXTRACTION | <0.1 | <1 | PASS |
| N-HEXANE | AT REFLUX TEMP’ FOR 7 HOURS | <0.1 | <175 | PASS |
| N-HEXANE | AT REFLUX TEMP FOR SUCCEEDING 2 HOURS OF EXTRACTION | <0.1 | <4 | PASS |
Notes:
1. mg/inch2 = milligram per square inch
2. °C = degrees Celsius
| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | DIN 53508 | 1.60 ± 0.05 | ASTM D297 | 1.60 ± 0.05 |
| HARDNESS | DIN 53505 | 65 ± 5 SH A | ASTM D2240 | 65 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | DIN 53504 | 716 PSI | ASTM D412 | 50 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | DIN 53504 | 250 | ASTM D412 | 250 |
| COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) | DIN ISO 815-1 | 30 | ASTM D395 METHOD B | 30 |
| TEAR RESISTANCE ( ANGULAR ) MIN | DIN 53515 | 196 LBS/INCH | ASTM D624 | 35 KG/CM |
| CHANGE IN PROPERTIES | ||||
| HEAT AGEING ( 72 HRS. AT 70 ºC ) | ASTM D573 | |||
| — HARDNESS (PTS) | + 5 (MAX) | + 5 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / – 15 | + 10 / – 15 | ||
| — ELONGATION AT BREAK (%) | + 10 / – 20 | + 10 / – 20 | ||
| VOLUME SWELL : AT 70º C FOR 72 HRS/IN | ASTM D 471 | |||
| IRM OIL NO.1 | + 2 % | + 2 % | ||
| IRM OIL NO.2 | + 15% | + 15% | ||
| IRM OIL NO.3 | + 45% | + 45% | ||
| POLYMER CONTENT (NEOPRENE) | 100% | 100% | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | FAIR | ASTM D 1149 | FAIR | |
| — DILUTE ACIDS AND BASES | GOOD | GOOD | ||
| — CONCENTRATED ACIDS AND BASES | FAIR | FAIR | ||
| — OILS | GOOD | GOOD | ||
| — SOLVENTS | FAIR | FAIR | ||
| TEMPERATURE RANGE | -30º TO + 130º C | -30º TO + 130º C | ||
| COLOUR | WHITE – RAL 1015 | |||
| EXTRACTANTS | TEST CONDITION | AMOUNT OF EXTRACTIVES (MG/INCH²) 1 | ACCEPTABLE LIMIT (MG/INCH²) | CONCLUSION |
| DISTILLED WATER | AT REFLUX TEMP’ FOR 7 HOURS | <0.1 | <20 | PASS |
| DISTILLER WATER | AT REFLUX TEMP FOR SUCCEEDING 2 HOURS OF EXTRACTION | <0.1 | <1 | PASS |
| N-HEXANE | AT REFLUX TEMP’ FOR 7 HOURS | <0.1 | <175 | PASS |
| N-HEXANE | AT REFLUX TEMP FOR SUCCEEDING 2 HOURS OF EXTRACTION | <0.1 | <4 | PASS |
Notes:
1. mg/inch2 = milligram per square inch
2. °C = degrees Celsius