‘Square Stud Pattern’ PVC Matting
- Attractive low relief square studded pattern
- Oil & Grease Resistant
- Clean & Hygienic
- Durable PVC compound
- Slip resistant multi-directional patterned surface
- Good floor to foot cold insulation properties
- Economically priced
- Cut lengths to order
Call for Price
Coru666 ‘Square Stud Pattern’ PVC Matting is an attractive and economic grade of PVC matting with a raised ‘Square Stud’ pattern design on one side and a plain, smooth reverse. Available in a choice of Black, Grey, Blue, Green or Red at 2.4mm stock thickness. Ideally suited for communal areas, walkways, tread mats, runners and general purpose industrial applications where a multi directional tread pattern is required.
This grade can be produced in varying width, length and thickness formats and in a variety of colours (RAL matched if needed) to special order. These would be subject to minimum batch run quantities, usually 500 M2 per size/colour.
| STOCK ROLL SIZES [M X M X MM] | WEIGHT [KG/M2] |
| 10m x 1.1m x 2.4mm | 3.5 |
| SPECIFICATIONS COMPOUND | VALUES [TYPICAL] |
| Colour | Black/Grey/Blue/Red/Green |
| Compound | PVC |
| Hardness [Shore A] | 75° |
| Density [SG] | 1.8 |
| Tensile Strength: [MPA] | 3.0 |
| Elongation [min] | 200% |
| Abrasion Resistance [mm³] | 250 |
| Minimum Temperature | -20°C |
| Maximum Temperature | +100°C |
| STOCK ROLL SIZES [M X M X MM] | WEIGHT [KG/M2] |
| 10m x 1.1m x 2.4mm | 3.5 |
| SPECIFICATIONS COMPOUND | VALUES [TYPICAL] |
| Colour | Black/Grey/Blue/Red/Green |
| Compound | PVC |
| Hardness [Shore A] | 75° |
| Density [SG] | 1.8 |
| Tensile Strength: [MPA] | 3.0 |
| Elongation [min] | 200% |
| Abrasion Resistance [mm³] | 250 |
| Minimum Temperature | -20°C |
| Maximum Temperature | +100°C |