Chemical Resistances
Coru213 Hydrogenated Nitrile 70° shore is a Sheeting for use with chemicals, oil, very high and very low temperatures.
N.B. Available in plain or self-adhesive backed tape (SAB) alternatives. Bespoke sheets and gaskets are available, as well as customised rubber strips. Email your enquiries to sales@coruba.co.uk.
The above sheeting is manufactured from top quality virgin materials and ingredients meeting high standard of performance.
- Material Profile: see below for exact specifications
- Thickness: 1mm to 6mm
- Sheet Size: 1.4m wide in 10m rolls
- Finish: Plate finish
- Cutting: Standard press-tools
This Product is REACH, RoHS, PAH and CE Compliant.
Other grades, colours and finishes are available – subject to minimum batch quantities.
|
Properties |
Test Method |
Values |
Tested Method |
Values |
|
FPS Units |
Metric Units |
|||
|
Specific Gravity |
DIN 53509 |
1.20 ± 0.05 |
ASTM D297 |
1.20 ± 0.05 |
|
Hardness |
DIN 53505 |
70 ± 5 Sh A |
ASTM D2240 |
70 ± 5 Sh A |
|
Tensile Strength (min) |
DIN 53504 |
1422 PSI |
ASTM D412 |
100kg/cm2 |
|
Elongation at Break (min) |
DIN 53504 |
200% |
ASTM D412 |
200% |
|
Compression Set (70oC/24hrs/25% set) (max) |
DIN 53517 |
50% |
ASTM D395 |
50% |
|
|
|
|
Method B |
|
|
Tear Resistance (Angular) (min) |
DIN 53515 |
250lbs/inch |
ASTM D624 |
45kg/cm |
|
Change in Properties |
|
|
|
|
|
Heat Ageing (72 hrs at 70oC) |
|
|
ASTM D573 |
|
|
– Hardness (Pts) |
|
+2 (Max) |
|
+2 (Max) |
|
– Tensile Strength (%) |
|
+5 |
|
5 |
|
– Elongation at Break (%) |
|
±10 |
|
±10 |
|
Volume Swell: At 70oC for 72 hrs/in |
|
|
ASTM D471 |
|
|
IRM No.901 |
|
1% |
|
1% |
|
IRM No.902 |
|
5% |
|
5% |
|
IRM No.903 |
|
10% |
|
10% |
|
Polymer Content (Hydrogenated Chemical Resistance) |
|
100% |
|
100% |
|
– Ozone |
|
Excellent |
ASTM D1149 |
Excellent |
|
– Dilute Acids and Bases |
|
Excellent |
|
Excellent |
|
– Concentrated Acids and Bases |
|
Fair |
|
Fair |
|
– Oils |
|
Excellent |
|
Excellent |
|
– Solvents |
|
Good |
|
Good |
|
Temperature Range |
|
-30o to 150oC |
|
-30o to 150oC |
|
Colour |
|
Black |
|
Black |
|
Properties |
Test Method |
Values |
Tested Method |
Values |
|
FPS Units |
Metric Units |
|||
|
Specific Gravity |
DIN 53509 |
1.20 ± 0.05 |
ASTM D297 |
1.20 ± 0.05 |
|
Hardness |
DIN 53505 |
70 ± 5 Sh A |
ASTM D2240 |
70 ± 5 Sh A |
|
Tensile Strength (min) |
DIN 53504 |
1422 PSI |
ASTM D412 |
100kg/cm2 |
|
Elongation at Break (min) |
DIN 53504 |
200% |
ASTM D412 |
200% |
|
Compression Set (70oC/24hrs/25% set) (max) |
DIN 53517 |
50% |
ASTM D395 |
50% |
|
|
|
|
Method B |
|
|
Tear Resistance (Angular) (min) |
DIN 53515 |
250lbs/inch |
ASTM D624 |
45kg/cm |
|
Change in Properties |
|
|
|
|
|
Heat Ageing (72 hrs at 70oC) |
|
|
ASTM D573 |
|
|
– Hardness (Pts) |
|
+2 (Max) |
|
+2 (Max) |
|
– Tensile Strength (%) |
|
+5 |
|
5 |
|
– Elongation at Break (%) |
|
±10 |
|
±10 |
|
Volume Swell: At 70oC for 72 hrs/in |
|
|
ASTM D471 |
|
|
IRM No.901 |
|
1% |
|
1% |
|
IRM No.902 |
|
5% |
|
5% |
|
IRM No.903 |
|
10% |
|
10% |
|
Polymer Content (Hydrogenated Chemical Resistance) |
|
100% |
|
100% |
|
– Ozone |
|
Excellent |
ASTM D1149 |
Excellent |
|
– Dilute Acids and Bases |
|
Excellent |
|
Excellent |
|
– Concentrated Acids and Bases |
|
Fair |
|
Fair |
|
– Oils |
|
Excellent |
|
Excellent |
|
– Solvents |
|
Good |
|
Good |
|
Temperature Range |
|
-30o to 150oC |
|
-30o to 150oC |
|
Colour |
|
Black |
|
Black |