High Grade Reinforced Coated Nylon Neoprene Gasket
- Generally conforms to BS2752-C60
- REACH, RoHS, PAH and CE compliant
- 1 ply 150 GSM Nylon: 60° Shore
- View material – Coru196CT
Call for Price
You save (%)
|
PROPERTIES |
TEST METHOD |
VALUES |
|
METRIC UNITS |
||
|
SPECIFIC GRAVITY |
BS 903: PART A1 |
1.30 |
|
HARDNESS |
BS 903: PART A26 |
60 ± 5 IRHD |
|
TENSILE STRENGTH (KG/CM2) |
BS 903: PART A2 |
130 |
|
ELONGATION AT BREAK (MIN) |
BS 903: PART A2 |
350% |
|
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
BS 903: PART A6 |
25% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
BS 903: PART A3 |
35 Kg/cm |
|
RESISTANCE TO ACCELERATED AGEING- 168HRS AT 70˚C |
BS 903: PART A19 |
|
|
— HARDNESS (Pts) |
BS 903: PART A26 |
+ 7 (MAX) |
|
— TENSILE STRENGTH (%) |
BS 903: PART A2 |
-12 (MAX) |
|
— ELONGATION AT BREAK (%) |
BS 903: PART A2 |
-20 (MAX) |
|
VOLUME SWELL: AT 40˚C FOR 24 HRS/IN |
BS 903: PART A16 |
|
|
FUEL B |
|
+ 70% (MAX) |
|
RESISTANCE TO LOW TEMPERATURE AT – 40ºC |
BS 903: PART A13 |
MEETS REQUIREMENTS |
|
ADHESION TO AND CORROSION OF METALS |
BS 903: PART A 37 |
MEETS REQUIREMENTS |
|
POLYMER CONTENT (NEOPRENE) |
|
100% |
|
ADDITIONAL INFORMATION – |
||
|
CHEMICAL RESISTANCE |
|
|
|
— OZONE |
BS 903: PART A 43 |
GOOD |
|
— DILUTE ACIDS AND BASES |
BS 903: PART A16 |
GOOD |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
— MINERAL OILS – PARAFINNIC & NAPHTHANIC HC |
|
GOOD |
|
— MINERAL OILS – AROMATIC HC |
|
FAIR |
|
–ANIMAL/VEGETABLE OIL |
|
GOOD |
|
–SOLVENTS |
|
FAIR |
|
TEMPERATURE RANGE |
|
-30º TO + 120º C |
|
COLOUR |
BLACK |
|
|
INSERTION |
1PLY 150GSM Nylon fabric reinforcement |
|
|
VOLUME SWELL DATA |
||
|
RESISTANCE TO LIQUIDS |
BS ISO 1817, 24 0 h at (40±1) °C −2 |
-0 |
|
VOLUME CHANGE (%) AFTER IMMERSION IN LIQUID B |
BS ISO 1817, 24 0 h at (40±1) °C −2 |
+70 |
|
RESISTANCE TO ACCELERATED AGEING |
PART A19, AIR-OVEN METHOD A, (168±2)h, (70±1)°C |
-0 |
|
CHANGE IN HARDNESS DEGREES (IRHD) |
PART A26, METHOD N, MEASUREMENTS BEFORE AND AFTER AGEING ON THE SAME 2 PLIES EACH 2.00MM THICK |
+7 |
|
MAXIMUM CHANGE IN TENSILE STRENGTH (% OF ORIGINAL VALUE) |
PART A2, TYPE 1 OR TYPE 2 DUMBBELLS |
-12 |
|
MAXIMUM CHANGE IN ELONGATION AT BREAK (% OF ORIGINAL VALUE) |
PART A2, TYPE 1 OR TYPE 2 DUMBBELLS |
-20 |
|
PROPERTIES |
TEST METHOD |
VALUES |
|
METRIC UNITS |
||
|
SPECIFIC GRAVITY |
BS 903: PART A1 |
1.30 |
|
HARDNESS |
BS 903: PART A26 |
60 ± 5 IRHD |
|
TENSILE STRENGTH (KG/CM2) |
BS 903: PART A2 |
130 |
|
ELONGATION AT BREAK (MIN) |
BS 903: PART A2 |
350% |
|
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
BS 903: PART A6 |
25% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
BS 903: PART A3 |
35 Kg/cm |
|
RESISTANCE TO ACCELERATED AGEING- 168HRS AT 70˚C |
BS 903: PART A19 |
|
|
— HARDNESS (Pts) |
BS 903: PART A26 |
+ 7 (MAX) |
|
— TENSILE STRENGTH (%) |
BS 903: PART A2 |
-12 (MAX) |
|
— ELONGATION AT BREAK (%) |
BS 903: PART A2 |
-20 (MAX) |
|
VOLUME SWELL: AT 40˚C FOR 24 HRS/IN |
BS 903: PART A16 |
|
|
FUEL B |
|
+ 70% (MAX) |
|
RESISTANCE TO LOW TEMPERATURE AT – 40ºC |
BS 903: PART A13 |
MEETS REQUIREMENTS |
|
ADHESION TO AND CORROSION OF METALS |
BS 903: PART A 37 |
MEETS REQUIREMENTS |
|
POLYMER CONTENT (NEOPRENE) |
|
100% |
|
ADDITIONAL INFORMATION – |
||
|
CHEMICAL RESISTANCE |
|
|
|
— OZONE |
BS 903: PART A 43 |
GOOD |
|
— DILUTE ACIDS AND BASES |
BS 903: PART A16 |
GOOD |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
— MINERAL OILS – PARAFINNIC & NAPHTHANIC HC |
|
GOOD |
|
— MINERAL OILS – AROMATIC HC |
|
FAIR |
|
–ANIMAL/VEGETABLE OIL |
|
GOOD |
|
–SOLVENTS |
|
FAIR |
|
TEMPERATURE RANGE |
|
-30º TO + 120º C |
|
COLOUR |
BLACK |
|
|
INSERTION |
1PLY 150GSM Nylon fabric reinforcement |
|
|
VOLUME SWELL DATA |
||
|
RESISTANCE TO LIQUIDS |
BS ISO 1817, 24 0 h at (40±1) °C −2 |
-0 |
|
VOLUME CHANGE (%) AFTER IMMERSION IN LIQUID B |
BS ISO 1817, 24 0 h at (40±1) °C −2 |
+70 |
|
RESISTANCE TO ACCELERATED AGEING |
PART A19, AIR-OVEN METHOD A, (168±2)h, (70±1)°C |
-0 |
|
CHANGE IN HARDNESS DEGREES (IRHD) |
PART A26, METHOD N, MEASUREMENTS BEFORE AND AFTER AGEING ON THE SAME 2 PLIES EACH 2.00MM THICK |
+7 |
|
MAXIMUM CHANGE IN TENSILE STRENGTH (% OF ORIGINAL VALUE) |
PART A2, TYPE 1 OR TYPE 2 DUMBBELLS |
-12 |
|
MAXIMUM CHANGE IN ELONGATION AT BREAK (% OF ORIGINAL VALUE) |
PART A2, TYPE 1 OR TYPE 2 DUMBBELLS |
-20 |