Free delivery on orders over £1200.00, all other orders have a fixed rate of £20.00 + VAT.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
Please note: All cut material is non-returnable unless faulty as these are non-sellable and have been cut to specific requirements.
Fuel Resistant Nitrile/PVC Strip
SKU: ST-Coru175
- Meets ASTM D 2000 M5 BG606A14B14C12EO34G21
- REACH, RoHS, PAH and CE compliant
- Fuel Resistant Grade
- High Quality NBR/PVC: 65° Shore
- View material – Coru175
Call for Price
Chemical Resistances
Brine, Calcium Chloride, Carbon Dioxide, Carbon Monoxide, Castor Oil, Corn Oil, Crude Oil, Diesel Oil, Fatty Acids, Gasoline, Glucose, Grease, Heptane, Hydraulic Fluid, Hydrogen Gas, Hydrogen Sulphide, Jet Fuels, Kerosene, Lard, Lime, Linoleic Acid, Linseed Oil, LPG, Lubricating Oils, Mineral Oil, Natural Gas, Neon Gas, Nitrogen, Oil Petroleum, Oleic Acid, Ozone, Paraffin Wax, Pentane, Petroleum Oils, Pine Oil, Propane, Sea Water, Sewage, Steam, Sulfuric Acid, Toluene, Transformer Oil, Urea, Varnish
Technical Information
| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | ASTM D297 | 1.25 | DIN 53508 | 1.25 |
| HARDNESS | ASTM D2240 | 65 ± 5 SH A | DIN 53505 | 65 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | ASTM D412 | 995 PSI | DIN 53504 | 60 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | ASTM D412 | 250% | DIN 53504 | 250% |
| COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) | ASTM D395 METHOD B | 35% | DIN 53517 | 35% |
| ABRASION LOSS (MAX) | ASTM D 5963 | 300 MM3 | DIN 53516 | 300 MM3 |
| TEAR RESISTANCE ( ANGULAR ) MIN | ASTM D624 | 123 LBS/INCH | DIN 53515 | 22 KG/CM |
| CHANGE IN PROPERTIES | ||||
| HEAT AGEING ( 72 HRS. AT 70ºC ) | ASTM D 573 | |||
| — HARDNESS (PTS) | + 6 (MAX) | + 6 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / -10 | + 10 / -10 | ||
| — ELONGATION AT BREAK (%) | + 10 / -20 | + 10 / -20 | ||
| VOLUME SWELL : AT 70ºC FOR 72 HRS/IN | ASTM D 471 | |||
| ASTM OIL NO.1 | -2% | -2% | ||
| ASTM OIL NO.2 | + 4% | + 4% | ||
| ASTM OIL NO.3 | + 13% | + 13% | ||
| AT FUEL B /24 HRS/ROOM TEMP, MAX | + 25 % | + 25 % | ||
| POLYMER CONTENT (NITRILE/PVC BLEND) | BLEND | BLEND | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | ASTM D 1149 | GOOD | GOOD | |
| — DILUTE ACIDS AND BASES | GOOD | GOOD | ||
| — CONCENTRATED ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — OILS | EXCELLENT | EXCELLENT |
| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | ASTM D297 | 1.25 | DIN 53508 | 1.25 |
| HARDNESS | ASTM D2240 | 65 ± 5 SH A | DIN 53505 | 65 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | ASTM D412 | 995 PSI | DIN 53504 | 60 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | ASTM D412 | 250% | DIN 53504 | 250% |
| COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) | ASTM D395 METHOD B | 35% | DIN 53517 | 35% |
| ABRASION LOSS (MAX) | ASTM D 5963 | 300 MM3 | DIN 53516 | 300 MM3 |
| TEAR RESISTANCE ( ANGULAR ) MIN | ASTM D624 | 123 LBS/INCH | DIN 53515 | 22 KG/CM |
| CHANGE IN PROPERTIES | ||||
| HEAT AGEING ( 72 HRS. AT 70ºC ) | ASTM D 573 | |||
| — HARDNESS (PTS) | + 6 (MAX) | + 6 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / -10 | + 10 / -10 | ||
| — ELONGATION AT BREAK (%) | + 10 / -20 | + 10 / -20 | ||
| VOLUME SWELL : AT 70ºC FOR 72 HRS/IN | ASTM D 471 | |||
| ASTM OIL NO.1 | -2% | -2% | ||
| ASTM OIL NO.2 | + 4% | + 4% | ||
| ASTM OIL NO.3 | + 13% | + 13% | ||
| AT FUEL B /24 HRS/ROOM TEMP, MAX | + 25 % | + 25 % | ||
| POLYMER CONTENT (NITRILE/PVC BLEND) | BLEND | BLEND | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | ASTM D 1149 | GOOD | GOOD | |
| — DILUTE ACIDS AND BASES | GOOD | GOOD | ||
| — CONCENTRATED ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — OILS | EXCELLENT | EXCELLENT |