Fuel Resistant Nitrile/PVC Gasket
- Meets ASTM D 2000 M5 BG606A14B14C12EO34G21
- REACH, RoHS, PAH and CE compliant
- Fuel Resistant Grade
- High Quality NBR/PVC: 65° Shore
- View material – Coru175
Call for Price
You save (%)
Chemical Resistances
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
ASTM D297 |
1.25 |
DIN 53508 |
1.25 |
|
HARDNESS |
ASTM D2240 |
65 ± 5 SH A |
DIN 53505 |
65 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
ASTM D412 |
995 PSI |
DIN 53504 |
60 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
ASTM D412 |
250% |
DIN 53504 |
250% |
|
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
ASTM D395 METHOD B |
35% |
DIN 53517 |
35% |
|
ABRASION LOSS (MAX) |
ASTM D 5963 |
300 MM3 |
DIN 53516 |
300 MM3 |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
ASTM D624 |
123 LBS/INCH |
DIN 53515 |
22 KG/CM |
|
CHANGE IN PROPERTIES |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 70ºC ) |
ASTM D 573 |
|
|
|
|
— HARDNESS (PTS) |
|
+ 6 (MAX) |
|
+ 6 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / -10 |
|
+ 10 / -10 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / -20 |
|
+ 10 / -20 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN |
ASTM D 471 |
|
|
|
|
ASTM OIL NO.1 |
|
-2% |
|
-2% |
|
ASTM OIL NO.2 |
|
+ 4% |
|
+ 4% |
|
ASTM OIL NO.3 |
|
+ 13% |
|
+ 13% |
|
AT FUEL B /24 HRS/ROOM TEMP, MAX |
|
+ 25 % |
|
+ 25 % |
|
POLYMER CONTENT (NITRILE/PVC BLEND) |
|
BLEND |
|
BLEND |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
ASTM D 1149 |
GOOD |
|
GOOD |
|
— DILUTE ACIDS AND BASES |
|
GOOD |
|
GOOD |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— OILS |
|
EXCELLENT |
|
EXCELLENT |
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
ASTM D297 |
1.25 |
DIN 53508 |
1.25 |
|
HARDNESS |
ASTM D2240 |
65 ± 5 SH A |
DIN 53505 |
65 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
ASTM D412 |
995 PSI |
DIN 53504 |
60 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
ASTM D412 |
250% |
DIN 53504 |
250% |
|
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
ASTM D395 METHOD B |
35% |
DIN 53517 |
35% |
|
ABRASION LOSS (MAX) |
ASTM D 5963 |
300 MM3 |
DIN 53516 |
300 MM3 |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
ASTM D624 |
123 LBS/INCH |
DIN 53515 |
22 KG/CM |
|
CHANGE IN PROPERTIES |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 70ºC ) |
ASTM D 573 |
|
|
|
|
— HARDNESS (PTS) |
|
+ 6 (MAX) |
|
+ 6 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / -10 |
|
+ 10 / -10 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / -20 |
|
+ 10 / -20 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN |
ASTM D 471 |
|
|
|
|
ASTM OIL NO.1 |
|
-2% |
|
-2% |
|
ASTM OIL NO.2 |
|
+ 4% |
|
+ 4% |
|
ASTM OIL NO.3 |
|
+ 13% |
|
+ 13% |
|
AT FUEL B /24 HRS/ROOM TEMP, MAX |
|
+ 25 % |
|
+ 25 % |
|
POLYMER CONTENT (NITRILE/PVC BLEND) |
|
BLEND |
|
BLEND |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
ASTM D 1149 |
GOOD |
|
GOOD |
|
— DILUTE ACIDS AND BASES |
|
GOOD |
|
GOOD |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— OILS |
|
EXCELLENT |
|
EXCELLENT |