Flame Retardant NFF16-101 M2-F3 UL94-VO Neoprene Gasket
- Fire Resistance to: NFF16-101 M2-F3 & DIN75200-UL94VO
- REACH, RoHS, PAH and CE compliant
- Chloroprene, Neoprene compound: 65° Shore
- View material – Coru215
Call for Price
You save (%)
Chemical Resistances
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
|
1.60 ± 0.05 |
DIN 53508 |
1.60 ± 0.05 |
|
HARDNESS |
ISO 48-4 |
65 ± 5 SH A |
ASTM D2240 |
65 ± 5 SH A |
|
TENSILE STRENGTH (MIN) |
ISO 37 |
711 PSI |
ASTM D412 |
50KG/CM2 |
|
ELONGATION AT BREAK (MIN) |
ISO 37 |
200% |
ASTM D142 |
200% |
|
COMPRESSION SET (70°C/24hrs/25% compression) (max) |
ISO 815-1 |
50% |
ASTM D395 METHOD B |
50% |
|
% TEAR RESISTANCE (ANGULAR) MIN |
ISO 34-1 |
112 lbs/inch |
ASTM D624 |
20Kg/cm |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING FOR (72 hrs. AT 70°C) |
|
|
ASTM D573 |
|
|
–HARDNESS (Pts) |
|
+5(Max) |
|
+5(Max) |
|
–TENSILE STRENGTH (%) |
|
+10/-20 |
|
+10/-20 |
|
ELONGATION AT BREAK (%) |
|
+10/-20 |
|
+10/-20 |
|
VOLUME SWELL: AT 70ºC for 72 hrs |
|
|
ASTM D471 |
|
|
In IRM OIL NO 901 |
|
+18% |
|
+18% |
|
In IRM OIL NO 902 |
|
23% |
|
+23% |
|
In IRM OIL NO 903 |
|
+60% |
|
+60% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
–OZONE (50 PPHM /20 DEG / 100 HRS) |
|
PASSES |
ASTM D1149 |
NO CRACKS |
|
DILUTE ACIDS AND BASES |
|
GOOD |
|
GOOD |
|
CONCENTRATED ACIDS AND BASES |
|
FAIR |
|
FAIR |
|
–OILS |
|
GOOD |
|
GOOD |
|
–SOLVENTS |
|
FAIR |
|
FAIR |
|
TEMPERATURE RANGE |
-30º to +100ºC |
|
-30º to +100ºC |
|
|
FIRE & SMOKE |
||||
|
FIRE – CLASSIFICATION |
NF F16-101 |
MEETS M2 REQUIREMENT |
NFF 16-101 |
MEETS M2 REQUIREMENT |
|
SMOKE CLASSIFICATION |
|
|
|
|
|
SMOKE DENSITY |
NF F16-101 |
MEETS F3 REQUIREMENT |
||
|
SMOKE TOXICITY |
NF F16-101 |
MEETS F3 REQUIREMENT |
||
|
UL94 VO |
PASS |
|||
|
COLOUR |
BLACK |
|||
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
|
1.60 ± 0.05 |
DIN 53508 |
1.60 ± 0.05 |
|
HARDNESS |
ISO 48-4 |
65 ± 5 SH A |
ASTM D2240 |
65 ± 5 SH A |
|
TENSILE STRENGTH (MIN) |
ISO 37 |
711 PSI |
ASTM D412 |
50KG/CM2 |
|
ELONGATION AT BREAK (MIN) |
ISO 37 |
200% |
ASTM D142 |
200% |
|
COMPRESSION SET (70°C/24hrs/25% compression) (max) |
ISO 815-1 |
50% |
ASTM D395 METHOD B |
50% |
|
% TEAR RESISTANCE (ANGULAR) MIN |
ISO 34-1 |
112 lbs/inch |
ASTM D624 |
20Kg/cm |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING FOR (72 hrs. AT 70°C) |
|
|
ASTM D573 |
|
|
–HARDNESS (Pts) |
|
+5(Max) |
|
+5(Max) |
|
–TENSILE STRENGTH (%) |
|
+10/-20 |
|
+10/-20 |
|
ELONGATION AT BREAK (%) |
|
+10/-20 |
|
+10/-20 |
|
VOLUME SWELL: AT 70ºC for 72 hrs |
|
|
ASTM D471 |
|
|
In IRM OIL NO 901 |
|
+18% |
|
+18% |
|
In IRM OIL NO 902 |
|
23% |
|
+23% |
|
In IRM OIL NO 903 |
|
+60% |
|
+60% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
–OZONE (50 PPHM /20 DEG / 100 HRS) |
|
PASSES |
ASTM D1149 |
NO CRACKS |
|
DILUTE ACIDS AND BASES |
|
GOOD |
|
GOOD |
|
CONCENTRATED ACIDS AND BASES |
|
FAIR |
|
FAIR |
|
–OILS |
|
GOOD |
|
GOOD |
|
–SOLVENTS |
|
FAIR |
|
FAIR |
|
TEMPERATURE RANGE |
-30º to +100ºC |
|
-30º to +100ºC |
|
|
FIRE & SMOKE |
||||
|
FIRE – CLASSIFICATION |
NF F16-101 |
MEETS M2 REQUIREMENT |
NFF 16-101 |
MEETS M2 REQUIREMENT |
|
SMOKE CLASSIFICATION |
|
|
|
|
|
SMOKE DENSITY |
NF F16-101 |
MEETS F3 REQUIREMENT |
||
|
SMOKE TOXICITY |
NF F16-101 |
MEETS F3 REQUIREMENT |
||
|
UL94 VO |
PASS |
|||
|
COLOUR |
BLACK |
|||