Physical Properties |
Test Method |
Unit |
0.3mm |
0.5mm |
0.8mm |
1mm |
|
Width |
– |
mm |
1400 |
1400 |
1400 |
1400 |
|
Length |
– |
M |
65 |
40 |
25 |
20 |
|
Hand |
– |
– |
3S |
3S |
3S |
3S |
|
Weight/ roll |
– |
kg |
34 |
35 |
35 |
35 |
|
Weight/ m2 |
– |
gr/m2 |
372 |
620 |
992 |
1240 |
|
Weight/ m |
– |
gr/m |
520 |
868 |
1390 |
1736 |
|
Finish |
– |
– |
Super Double Polished |
|||
|
Colour |
– |
– |
Crystal Clear |
|||
|
UV Stabilised |
– |
– |
Yes |
Yes |
Yes |
Yes |
|
Fire Retardant |
NF P92-507 DIN 4102-1 |
– |
– |
– |
– |
– |
|
Low-Temperature Brittleness (Impact) |
ASTM D746 |
ºC |
-40 |
-40 |
-35 |
-30 |
|
Tear Resistance |
ASTM D1004-13 |
N |
21.2 (X) 19.8 (Y) |
34.2 (X) 32.2 (Y) |
58.5 (X) 56.3 (Y) |
69.5 (X) 66.7 (Y) |
|
Tensile Strength |
ISO 527-1:2012 ISO 527-3:2001 |
MPa |
25.6 (X) 29.3 (Y) |
23.7 (X) 25.3 (Y) |
24.2 (X) 27.4 (Y) |
20.5 (X) 25.5 (Y) |
|
Elongation At Break |
ISO 527-1:2012 ISO 527-3:2001 |
% |
350 (X) 320 (Y) |
360 (X) 310 (Y) |
370 (X) 350 (Y) |
380 (X) 420 (Y) |
|
Heat Shrinkage (80ºC 10min) |
DIN 53377:2007 |
% |
0.7 (X) -2.2 (Y) |
0.6 (X) -2.9 (Y) |
1.0 (X) -2.8 (Y) |
0.9 (X) -2.9 (Y) |
|
Physical Properties |
Test Method |
Unit |
0.3mm |
0.5mm |
0.8mm |
1mm |
|
Width |
– |
mm |
1400 |
1400 |
1400 |
1400 |
|
Length |
– |
M |
65 |
40 |
25 |
20 |
|
Hand |
– |
– |
3S |
3S |
3S |
3S |
|
Weight/ roll |
– |
kg |
34 |
35 |
35 |
35 |
|
Weight/ m2 |
– |
gr/m2 |
372 |
620 |
992 |
1240 |
|
Weight/ m |
– |
gr/m |
520 |
868 |
1390 |
1736 |
|
Finish |
– |
– |
Super Double Polished |
|||
|
Colour |
– |
– |
Crystal Clear |
|||
|
UV Stabilised |
– |
– |
Yes |
Yes |
Yes |
Yes |
|
Fire Retardant |
NF P92-507 DIN 4102-1 |
– |
– |
– |
– |
– |
|
Low-Temperature Brittleness (Impact) |
ASTM D746 |
ºC |
-40 |
-40 |
-35 |
-30 |
|
Tear Resistance |
ASTM D1004-13 |
N |
21.2 (X) 19.8 (Y) |
34.2 (X) 32.2 (Y) |
58.5 (X) 56.3 (Y) |
69.5 (X) 66.7 (Y) |
|
Tensile Strength |
ISO 527-1:2012 ISO 527-3:2001 |
MPa |
25.6 (X) 29.3 (Y) |
23.7 (X) 25.3 (Y) |
24.2 (X) 27.4 (Y) |
20.5 (X) 25.5 (Y) |
|
Elongation At Break |
ISO 527-1:2012 ISO 527-3:2001 |
% |
350 (X) 320 (Y) |
360 (X) 310 (Y) |
370 (X) 350 (Y) |
380 (X) 420 (Y) |
|
Heat Shrinkage (80ºC 10min) |
DIN 53377:2007 |
% |
0.7 (X) -2.2 (Y) |
0.6 (X) -2.9 (Y) |
1.0 (X) -2.8 (Y) |
0.9 (X) -2.9 (Y) |