Coru106 Black Neoprene (10% content) / SBR Rubber 70° shore. It is used where a cheaper quality material will suit – in simple applications such as packing pieces, dust seals, protection pads etc. where the material is not coming under any duress and slight resistance is required.
N.B. Available in plain or self-adhesive backed tape (SAB) alternatives. Bespoke sheets and gaskets are available, as well as customised rubber strips. Email your enquiries to sales@coruba.co.uk.
Material Profile (See Below):
Other grades, colours and finishes are available - subject to minimum batch quantities.
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
SPECIFIC GRAVITY |
DIN 53508 |
1.45 ± 0.05 |
ASTM D297 |
1.45 ± 0.05 |
HARDNESS |
DIN 53505 |
70 ± 5 SH A |
ASTM D2240 |
70 ± 5 SH A |
TENSILE STRENGTH (MIN) |
DIN 53504 |
569 PSI |
ASTM D412 |
40 KG/CM2 |
ELONGATION AT BREAK (MIN) |
DIN 53504 |
200% |
ASTM D412 |
200% |
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) |
DIN ISO 815-1 |
40% |
ASTM D395 METHOD B |
40% |
TEAR RESISTANCE (ANGULAR) MIN |
DIN 53515 |
100 LBS/INCH |
ASTM D624 |
18 KG/CM |
CHANGE IN PROPERTIES |
|
|
|
|
HEAT AGEING (72 HRS. AT 70 ºC) |
|
|
ASTM D573 |
|
--- HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
--- TENSILE STRENGTH (%) |
|
+ 10 / - 25 |
|
+ 10 / - 25 |
--- ELONGATION AT BREAK (%) |
|
+ 10 / - 25 |
|
+ 10 / - 25 |
VOLUME SWELL : AT 70º C FOR 72 HRS/IN |
|
|
ASTM D 471 |
|
IRM OIL NO.1 |
|
+ 33% |
|
+ 33% |
IRM OIL NO.2 |
|
+ 47% |
|
+ 47% |
IRM OIL NO.3 |
|
+ 90% |
|
+ 90% |
POLYMER CONTENT (NEOPRENE) |
|
10% |
|
10% |
CHEMICAL RESISTANCE |
|
|
|
|
--- OZONE |
|
FAIR |
ASTM D 1149 |
FAIR |
--- DILUTE ACIDS AND BASES |
|
FAIR |
|
FAIR |
--- CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
--- OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
--- SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
TEMPERATURE RANGE |
|
-30 º TO +90º C |
|
-30 º TO +90º C |
COLOUR |
|
BLACK |
Special Price | No |
---|---|
Resistance to | Please Call |
Insertion Req | No |
Material | Neoprene / SBR Blended - Economy Grade |
Shore Hardness +/- 5º | 70 |