Black High Abrasion Grade 60° shore – Antistatic ASTM D257
- Meets ASTM D 2000 M2 AA612A13B13C12G21J1
- REACH, RoHS, PAH and CE compliant
- High Abrasion Resistant
- Suitable for applications such as snow plough rubbers, scraper blades, wipers and hard chute lining
- Natural Rubber: 60° Shore
- Anti-Static: ASTM D257 105 to 109
From £45.02 Excl. VAT
This product is available for bespoke manufacturing, please choose an option below:
Coru152 Black High Abrasion Grade 60° Shore is a high abrasion resistant rubber sheet material particularly suitable for applications such as snow plough rubbers, scraper blades, wipers and hard chute lining. It is a Styrene Butadiene Rubber with a hardness of 60° shore.
Thickness’ of 15mm to 25mm are available with heavy-duty fabric backing SM151D.
N.B. Available in plain or self-adhesive backed tape (SAB) alternatives. Bespoke sheets and gaskets are available, as well as customised rubber strips. Email your enquiries to sales@coruba.co.uk.
The above sheeting is manufactured from top quality virgin materials and ingredients meeting high standard of performance.
Material Profile (see below):
- Thickness: 1.5mm to 25mm
- Sheet Size: 1.4m wide in 10m rolls
- Finish: Plate finish
- Cutting: Standard press-tools (full steel construction advised)
- This Product is REACH, RoHS, PAH and CE Compliant
Other grades, colours and finishes are available – subject to minimum batch quantities.
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.17±0.05 |
ASTM D297 |
1.17±0.05 |
|
HARDNESS |
DIN 53505 |
60 ± 5 SH A |
ASTM D2240 |
60 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
DIN 53504 |
1638 PSI |
ASTM D412 |
115 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
450% |
ASTM D412 |
450% |
|
ABRASION RESISTANCE ( MAX ) |
DIN 53516 |
120 MM3 |
ASTM D5963 |
120 MM3 |
|
COMPRESSION SET (70ºC/24 HRS/25% COMPRESSION) (MAX) |
DIN ISO 815-1 |
30% |
ASTM D395 METHOD B |
30% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
168 LBS/INCH |
ASTM D624 |
30 KG/CM |
|
ANTISTATIC CHARACTERISTIC |
ASTM D257 |
105 to 109 |
ASTM D257 |
105 to 109 |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING FOR ( 72 HRS. AT 70ºC ) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS |
|
|
ASTM D 471 |
|
|
IN IRM OIL NO.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
IN IRM OIL NO.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
IN IRM OIL NO.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
FAIR |
ASTM D 1149 |
FAIR |
|
— DILUTE ACIDS AND BASES |
|
GOOD |
|
GOOD |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-25º TO + 70ºC |
|
-25º TO + 70ºC |
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.17±0.05 |
ASTM D297 |
1.17±0.05 |
|
HARDNESS |
DIN 53505 |
60 ± 5 SH A |
ASTM D2240 |
60 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
DIN 53504 |
1638 PSI |
ASTM D412 |
115 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
450% |
ASTM D412 |
450% |
|
ABRASION RESISTANCE ( MAX ) |
DIN 53516 |
120 MM3 |
ASTM D5963 |
120 MM3 |
|
COMPRESSION SET (70ºC/24 HRS/25% COMPRESSION) (MAX) |
DIN ISO 815-1 |
30% |
ASTM D395 METHOD B |
30% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
168 LBS/INCH |
ASTM D624 |
30 KG/CM |
|
ANTISTATIC CHARACTERISTIC |
ASTM D257 |
105 to 109 |
ASTM D257 |
105 to 109 |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING FOR ( 72 HRS. AT 70ºC ) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS |
|
|
ASTM D 471 |
|
|
IN IRM OIL NO.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
IN IRM OIL NO.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
IN IRM OIL NO.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
FAIR |
ASTM D 1149 |
FAIR |
|
— DILUTE ACIDS AND BASES |
|
GOOD |
|
GOOD |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-25º TO + 70ºC |
|
-25º TO + 70ºC |