Coru1458 Black EPDM (100% content) 80° shore. Meeting ICI M228.
High Acid Resistance (Please call to confirm suitability
N.B. Available in plain or self-adhesive backed tape (SAB) alternatives. Bespoke sheets and gaskets are available, as well as customised rubber strips. Email your enquiries to sales@coruba.co.uk.
Material Profile (See Below):
Other grades, colours and finishes are available - subject to minimum batch quantities.
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
SPECIFIC GRAVITY |
ASTM D297 |
1.38 ± 0.05 |
DIN 53508 |
1.38 ± 0.05 |
HARDNESS |
ASTM D2240 |
80 ± 5 SH A |
DIN 53505 |
80 ± 5 SH A |
TENSILE STRENGTH ( MIN ) |
ASTM D412 |
1015 PSI |
DIN 53504 |
70 KG/CM2 |
ELONGATION AT BREAK ( MIN ) |
ASTM D412 |
250% |
DIN 53504 |
250% |
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
ASTM D395 METHOD B |
35% |
DIN 53517 |
35% |
TEAR RESISTANCE ( ANGULAR ) MIN |
ASTM D624 |
110 LBS/INCH |
DIN 53515 |
20 KG/CM |
CHANGE IN PROPERTIES |
|
|
|
|
HEAT AGEING ( 72 HRS. AT 70ºC ) |
ASTM D573 |
|
|
|
--- HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
--- TENSILE STRENGTH (%) |
|
+ 10 / - 10 |
|
+ 10 / - 10 |
--- ELONGATION AT BREAK (%) |
|
+ 10 / - 10 |
|
+ 10 / - 10 |
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN |
ASTM D 471 |
|
|
|
ASTM OIL NO.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
ASTM OIL NO.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
ASTM OIL NO.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
POLYMER CONTENT (EPDM) |
|
100% |
|
100% |
CARBON CONTENT |
|
30% |
|
30% |
CHEMICAL RESISTANCE |
|
|
|
|
--- OZONE |
ASTM D 1149 |
EXCELLENT |
|
EXCELLENT |
--- DILUTE ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
--- CONCENTRATED ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
--- OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
--- SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
TEMPERATURE RANGE |
|
-30º TO + 130ºC |
|
-30º TO + 130ºC |
COLOUR |
|
BLACK |
Colour | Black |
---|---|
Special Price | No |
Width | 1.6m |
Resistance to | Acid (Please Call) |
Insertion Req | No |
Material | EPDM - High Grade |
Shore Hardness +/- 5º | 80 |
Download Document |
---|