Black High Temperature FKM A Rubber Sheeting 75° shore
- Good flame resistance
- Resistant to weather ageing
- High temperature compression resistance
- Good solvent, chemical and hydrocarbon resistance
- Chemical resistant
From £121.89 Excl. VAT
You save (%)
This product is available for bespoke manufacturing, please choose an option below:
Coru148 Black High Temperature FKM A Rubber 75° shore is a FKM or Fluoro Elastomer with 65% Fluorine content which offers high resistance to temperatures up to 205° C.
- Material Profile: See below
- Thickness: 0.5mm to 12mm, other thicknesses by application
- Sheet Size: 1.2m wide in 10m rolls, thicknesses 8mm and over in 5m Rolls
- Finish: Smooth finish,
- Cutting: Standard press-tools
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
2.0 |
ASTM D297 |
2.0 |
|
HARDNESS |
DIN 53505 |
75 ± 5 SH A |
ASTM D2240 |
75 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
DIN 53504 |
853 PSI |
ASTM D412 |
60 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
200% |
ASTM D412 |
200% |
|
COMPRESSION SET (175 ºC/22 HRS/25% SET) (MAX) |
DIN 53517 |
55% |
ASTM D395 METHOD B |
55% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
213 LBS/INCH |
ASTM D624 |
15 KG/CM |
|
CHANGE IN PROPERTIES |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 150 ºC ) |
|
|
ASTM D573 |
|
|
HARDNESS (PTS) |
|
≤10sh |
|
≤10sh |
|
TENSILE STRENGTH (%) |
|
≤10% |
|
≤10% |
|
ELONGATION AT BREAK (%) |
|
≤25% |
|
≤25% |
|
VOLUME SWELL : AT 150º C FOR 24 HRS/IN |
|
|
ASTM D 471 |
|
|
ASTM OIL NO.1 |
|
– 6% |
|
– 6% |
|
ASTM OIL NO.2 |
|
– 1% |
|
– 1% |
|
ASTM OIL NO.3 |
|
+ 5% |
|
+ 5% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
OZONE |
|
EXCELLENT |
ASTM D 1149 |
EXCELLENT |
|
DILUTE ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
CONCENTRATED ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
OILS |
|
VERY GOOD |
|
VERY GOOD |
|
SOLVENTS |
|
VERY GOOD |
|
VERY GOOD |
|
TEMPERATURE RANGE |
|
-20º TO + 205º C |
|
-20º TO + 205º C |
|
COLOUR |
Black |
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
2.0 |
ASTM D297 |
2.0 |
|
HARDNESS |
DIN 53505 |
75 ± 5 SH A |
ASTM D2240 |
75 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
DIN 53504 |
853 PSI |
ASTM D412 |
60 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
200% |
ASTM D412 |
200% |
|
COMPRESSION SET (175 ºC/22 HRS/25% SET) (MAX) |
DIN 53517 |
55% |
ASTM D395 METHOD B |
55% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
213 LBS/INCH |
ASTM D624 |
15 KG/CM |
|
CHANGE IN PROPERTIES |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 150 ºC ) |
|
|
ASTM D573 |
|
|
HARDNESS (PTS) |
|
≤10sh |
|
≤10sh |
|
TENSILE STRENGTH (%) |
|
≤10% |
|
≤10% |
|
ELONGATION AT BREAK (%) |
|
≤25% |
|
≤25% |
|
VOLUME SWELL : AT 150º C FOR 24 HRS/IN |
|
|
ASTM D 471 |
|
|
ASTM OIL NO.1 |
|
– 6% |
|
– 6% |
|
ASTM OIL NO.2 |
|
– 1% |
|
– 1% |
|
ASTM OIL NO.3 |
|
+ 5% |
|
+ 5% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
OZONE |
|
EXCELLENT |
ASTM D 1149 |
EXCELLENT |
|
DILUTE ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
CONCENTRATED ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
OILS |
|
VERY GOOD |
|
VERY GOOD |
|
SOLVENTS |
|
VERY GOOD |
|
VERY GOOD |
|
TEMPERATURE RANGE |
|
-20º TO + 205º C |
|
-20º TO + 205º C |
|
COLOUR |
Black |