Black Neoprene (10% content) / SBR Rubber 70° shore
- Meets ASTM D 2000 M3 BC604A14B14EO34G21
- REACH, RoHS, PAH and CE compliant
- An excellent economy option
- Neoprene/SBR rubber: 70° Shore
From £8.12 Excl. VAT
This product is available for bespoke manufacturing, please choose an option below:
Coru106 Black Neoprene (10% content) / SBR Rubber 70° shore. It is an excellent economy option – in simple applications such as packing pieces, dust seals, protection pads etc. where the material is not coming under any duress and slight resistance is required.
N.B. Available in plain or self-adhesive backed tape (SAB) alternatives. Bespoke sheets and gaskets are available, as well as customised rubber strips. Email your enquiries to sales@coruba.co.uk.
Material Profile (See Below):
- Thickness: 1.5 mm to 50mm
- Sheet Size: 1.4m wide in 5m and 10m rolls
- Finish: Smooth finish
- Cutting: Standard press-tools
Other grades, colours and finishes are available – subject to minimum batch quantities.
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.50 ± 0.05 |
ASTM D297 |
1.70 ± 0.05 |
|
HARDNESS |
DIN 53505 |
70 ± 5 SH A |
ASTM D2240 |
70 ± 5 SH A |
|
TENSILE STRENGTH (MIN) |
DIN 53504 |
497 PSI |
ASTM D412 |
35 KG/CM2 |
|
ELONGATION AT BREAK (MIN) |
DIN 53504 |
200% |
ASTM D412 |
200% |
|
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) |
DIN 53517 |
50% |
ASTM D395 METHOD B |
50% |
|
TEAR RESISTANCE (ANGULAR) MIN |
DIN 53515 |
84 LBS/INCH |
ASTM D624 |
15 KG/CM |
|
CHANGE IN PROPERTIES |
|
|
|
|
|
HEAT AGEING (72 HRS. AT 70 ºC) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
VOLUME SWELL : AT 70º C FOR 72 HRS/IN |
|
|
ASTM D 471 |
|
|
IRM OIL NO.1 |
|
+ 33% |
|
+ 33% |
|
IRM OIL NO.2 |
|
+ 47% |
|
+ 47% |
|
IRM OIL NO.3 |
|
+ 90% |
|
+ 90% |
|
POLYMER CONTENT (NEOPRENE) |
|
10% |
|
10% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
FAIR |
ASTM D 1149 |
FAIR |
|
— DILUTE ACIDS AND BASES |
|
FAIR |
|
FAIR |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-30º TO +70º C |
|
-30º TO +70º C |
|
COLOUR |
|
BLACK |
||
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.50 ± 0.05 |
ASTM D297 |
1.70 ± 0.05 |
|
HARDNESS |
DIN 53505 |
70 ± 5 SH A |
ASTM D2240 |
70 ± 5 SH A |
|
TENSILE STRENGTH (MIN) |
DIN 53504 |
497 PSI |
ASTM D412 |
35 KG/CM2 |
|
ELONGATION AT BREAK (MIN) |
DIN 53504 |
200% |
ASTM D412 |
200% |
|
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) |
DIN 53517 |
50% |
ASTM D395 METHOD B |
50% |
|
TEAR RESISTANCE (ANGULAR) MIN |
DIN 53515 |
84 LBS/INCH |
ASTM D624 |
15 KG/CM |
|
CHANGE IN PROPERTIES |
|
|
|
|
|
HEAT AGEING (72 HRS. AT 70 ºC) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
VOLUME SWELL : AT 70º C FOR 72 HRS/IN |
|
|
ASTM D 471 |
|
|
IRM OIL NO.1 |
|
+ 33% |
|
+ 33% |
|
IRM OIL NO.2 |
|
+ 47% |
|
+ 47% |
|
IRM OIL NO.3 |
|
+ 90% |
|
+ 90% |
|
POLYMER CONTENT (NEOPRENE) |
|
10% |
|
10% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
FAIR |
ASTM D 1149 |
FAIR |
|
— DILUTE ACIDS AND BASES |
|
FAIR |
|
FAIR |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-30º TO +70º C |
|
-30º TO +70º C |
|
COLOUR |
|
BLACK |
||