Black Shotblast Natural Rubber 50° shore
- Meets ASTM D 2000 M2 AA505A13B13G21
- REACH, RoHS, PAH and CE compliant
- Medium grade abrasion resistance
- Natural Rubber: 50° Shore
From £15.44 Excl. VAT
This product is available for bespoke manufacturing, please choose an option below:
Coru1310 Black Shotblast Natural Rubber 50° shore is a high quality Shot Blast polymeric sheeting for applications including shotblast, chute linings, conveyor skirts and wear strips with good resistance to dilute acids and alkalis.
N.B. Available in plain or self-adhesive backed tape (SAB) alternatives. Bespoke sheets and gaskets are available, as well as customised rubber strips. Email your enquiries to sales@coruba.co.uk.
Material Profile (see below):
- Thickness: 1mm to 25mm
- Sheet Size: 1.4m wide in 5m and 10m rolls
- Finish: Smooth finish
- Cutting: Standard press-tools
Other grades, colours and finishes are available – subject to minimum batch quantities.
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.35±0.05 |
ASTM D297 |
1.35±0.05 |
|
HARDNESS |
DIN 53505 |
50 ± 5 SH A |
ASTM D2240 |
50 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
DIN 53504 |
711 PSI |
ASTM D412 |
50 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
300% |
ASTM D412 |
300% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
112 LBS/INCH |
ASTM D624 |
20 KG/CM |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING FOR ( 72 HRS. AT 70 ºC ) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / -15 |
|
+ 10 / -15 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / -25 |
|
+ 10 / -25 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS |
|
|
ASTM D 471 |
|
|
IN IRM OIL NO.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
IN IRM OIL NO.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
IN IRM OIL NO.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
NOT RECOMMENDED |
ASTM D 1149 |
NOT RECOMMENDED |
|
— DILUTE ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-30º TO + 70 ºC |
|
-30º TO + 70 ºC |
|
COLOUR |
|
BLACK |
||
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.35±0.05 |
ASTM D297 |
1.35±0.05 |
|
HARDNESS |
DIN 53505 |
50 ± 5 SH A |
ASTM D2240 |
50 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
DIN 53504 |
711 PSI |
ASTM D412 |
50 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
300% |
ASTM D412 |
300% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
112 LBS/INCH |
ASTM D624 |
20 KG/CM |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING FOR ( 72 HRS. AT 70 ºC ) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / -15 |
|
+ 10 / -15 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / -25 |
|
+ 10 / -25 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS |
|
|
ASTM D 471 |
|
|
IN IRM OIL NO.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
IN IRM OIL NO.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
IN IRM OIL NO.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
NOT RECOMMENDED |
ASTM D 1149 |
NOT RECOMMENDED |
|
— DILUTE ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-30º TO + 70 ºC |
|
-30º TO + 70 ºC |
|
COLOUR |
|
BLACK |
||