Blue Metal Detectable FDA Approved Neoprene Gasket
- Approved to FDA 21 CFR 177.2600 – EU1935/2004 Compliant
- REACH, RoHS, PAH and CE compliant
- Metal Detectable Silicone: 65° Shore
- View material – Coru168
Call for Price
You save (%)
Chemical Resistances
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.50 ± 0.05 |
ASTM D297 |
1.50 ± 0.05 |
|
HARDNESS |
DIN 53505 |
65 ± 5 SH A |
ASTM D2240 |
65 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
DIN 53504 |
1990PSI |
ASTM D412 |
140 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
600% |
ASTM D412 |
600% |
|
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
DIN 53517 |
50% |
ASTM D395 METHOD B |
50% |
|
POLYMER CONTENT (%) |
|
100 |
|
100 |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
170 LBS/INCH |
ASTM D624 |
30 KG/CM |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 70 ºC ) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / – 30 |
|
+ 10 / – 30 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN |
|
|
ASTM D 471 |
|
|
IRM OIL NO.1 |
|
+18% |
|
+18% |
|
IRM OIL NO.2 |
|
+23% |
|
+23% |
|
IRM OIL NO.3 |
|
+60% |
|
+60% |
|
POLYMER CONTENT (NEOPRENE) |
|
100% |
|
100% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
GOOD |
ASTM D 1149 |
GOOD |
|
— DILUTE ACIDS AND BASES |
|
GOOD |
|
GOOD |
|
— CONCENTRATED ACIDS AND BASES |
|
FAIR |
|
FAIR |
|
— OILS |
|
GOOD |
|
GOOD |
|
— SOLVENTS |
|
FAIR |
|
FAIR |
|
TEMPERATURE RANGE |
|
-25º TO + 120º C |
|
-25º TO + 120º C |
|
COLOUR |
|
BLUE |
||
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.50 ± 0.05 |
ASTM D297 |
1.50 ± 0.05 |
|
HARDNESS |
DIN 53505 |
65 ± 5 SH A |
ASTM D2240 |
65 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
DIN 53504 |
1990PSI |
ASTM D412 |
140 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
600% |
ASTM D412 |
600% |
|
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
DIN 53517 |
50% |
ASTM D395 METHOD B |
50% |
|
POLYMER CONTENT (%) |
|
100 |
|
100 |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
DIN 53515 |
170 LBS/INCH |
ASTM D624 |
30 KG/CM |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 70 ºC ) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / – 25 |
|
+ 10 / – 25 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / – 30 |
|
+ 10 / – 30 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN |
|
|
ASTM D 471 |
|
|
IRM OIL NO.1 |
|
+18% |
|
+18% |
|
IRM OIL NO.2 |
|
+23% |
|
+23% |
|
IRM OIL NO.3 |
|
+60% |
|
+60% |
|
POLYMER CONTENT (NEOPRENE) |
|
100% |
|
100% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
GOOD |
ASTM D 1149 |
GOOD |
|
— DILUTE ACIDS AND BASES |
|
GOOD |
|
GOOD |
|
— CONCENTRATED ACIDS AND BASES |
|
FAIR |
|
FAIR |
|
— OILS |
|
GOOD |
|
GOOD |
|
— SOLVENTS |
|
FAIR |
|
FAIR |
|
TEMPERATURE RANGE |
|
-25º TO + 120º C |
|
-25º TO + 120º C |
|
COLOUR |
|
BLUE |
||