Free delivery on orders over £1200.00, all other orders have a fixed rate of £20.00 + VAT.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
Please note: All cut material is non-returnable unless faulty as these are non-sellable and have been cut to specific requirements.
Premium Grade NR/SBR Gasket
SKU: GSKT-Coru101
- Meets ASTM D 2000 M2 AA416A13B13C12G21J1
- REACH, RoHS, PAH and CE compliant
- For use where a cheaper material will suit
- Premium Grade NR/SBR blend: 40° Shore
- View material – Coru101
Call for Price
You save (%)
Technical Information
| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | DIN 53508 | 1.35±0.05 | ASTM D297 | 1.35±0.05 |
| HARDNESS | DIN 53505 | 40 ± 5 SH A | ASTM D2240 | 40 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | DIN 53504 | 713 PSI | ASTM D412 | 40 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | DIN 53504 | 250% | ASTM D412 | 250% |
| COMPRESSION SET (70ºC/24 HRS/25% COMPRESSION) (MAX) | DIN 53517 | 40% | ASTM D395 METHOD B | 40% |
| TEAR RESISTANCE ( ANGULAR ) MIN | DIN 53515 | 112 LBS/INCH | ASTM D624 | 20 KG/CM |
| CHANGE IN PROPERTIES AFTER | ||||
| HEAT AGEING FOR ( 72 HRS. AT 70 ºC ) | ASTM D573 | |||
| — HARDNESS (PTS) | + 5 (MAX) | + 5 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / -25 | + 10 / -25 | ||
| — ELONGATION AT BREAK (%) | + 10 / -25 | + 10 / -25 | ||
| VOLUME SWELL : AT 70ºC FOR 72 HRS | ASTM D 471 | |||
| IN IRM OIL NO.1 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.2 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.3 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | NOT RECOMMENDED | ASTM D 1149 | NOT RECOMMENDED | |
| — DILUTE ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — CONCENTRATED ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — OILS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — SOLVENTS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| TEMPERATURE RANGE | -20º TO + 70 ºC | -20º TO + 70 ºC | ||
| COLOUR | BLACK | |||
| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | DIN 53508 | 1.35±0.05 | ASTM D297 | 1.35±0.05 |
| HARDNESS | DIN 53505 | 40 ± 5 SH A | ASTM D2240 | 40 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | DIN 53504 | 713 PSI | ASTM D412 | 40 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | DIN 53504 | 250% | ASTM D412 | 250% |
| COMPRESSION SET (70ºC/24 HRS/25% COMPRESSION) (MAX) | DIN 53517 | 40% | ASTM D395 METHOD B | 40% |
| TEAR RESISTANCE ( ANGULAR ) MIN | DIN 53515 | 112 LBS/INCH | ASTM D624 | 20 KG/CM |
| CHANGE IN PROPERTIES AFTER | ||||
| HEAT AGEING FOR ( 72 HRS. AT 70 ºC ) | ASTM D573 | |||
| — HARDNESS (PTS) | + 5 (MAX) | + 5 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / -25 | + 10 / -25 | ||
| — ELONGATION AT BREAK (%) | + 10 / -25 | + 10 / -25 | ||
| VOLUME SWELL : AT 70ºC FOR 72 HRS | ASTM D 471 | |||
| IN IRM OIL NO.1 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.2 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.3 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | NOT RECOMMENDED | ASTM D 1149 | NOT RECOMMENDED | |
| — DILUTE ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — CONCENTRATED ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — OILS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — SOLVENTS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| TEMPERATURE RANGE | -20º TO + 70 ºC | -20º TO + 70 ºC | ||
| COLOUR | BLACK | |||