Free delivery on orders over £1200.00, all other orders have a fixed rate of £20.00 + VAT.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
Please note: All cut material is non-returnable unless faulty as these are non-sellable and have been cut to specific requirements.
Tan Shotblast Grade Natural Rubber Gasket
SKU: GSKT-Coru150
- Meets ASTM D 2000 M2 AA412A13B13C12G21J1
- Ideal for Shotblast
- Ideal for abrasion resistant applications
- Natural Rubber: 45° Shore
- Tan – RAL 1013
- View material – Coru150
Call for Price
You save (%)
Technical Information
| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | DIN 53508 | 1.20 ±0.05 | ASTM D297 | 1.20 ±0.05 |
| HARDNESS | DIN 53505 | 45 ± 5 SH A | ASTM D2240 | 45 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | DIN 53504 | 1425 PSI | ASTM D412 | 100 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | DIN 53504 | 400% | ASTM D412 | 400% |
| ABRASION RESISTANCE ( MAX ) | DIN 53516 | 150 MM3 | ASTM D5963 | 150 MM3 |
| COMPRESSION SET (70ºC/24 HRS/25% COMPRESSION) (MAX) | DIN 53517 | 35% | ASTM D395 METHOD B | 35% |
| TEAR RESISTANCE ( ANGULAR ) MIN | DIN 53515 | 140 LBS/INCH | ASTM D624 | 25 KG/CM |
| CHANGE IN PROPERTIES AFTER | ||||
| HEAT AGEING FOR ( 72 HRS. AT 70 ºC ) | ASTM D573 | |||
| — HARDNESS (PTS) | + 5 (MAX) | + 5 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / – 20 | + 10 / – 20 | ||
| — ELONGATION AT BREAK (%) | + 10 / – 20 | + 10 / – 20 | ||
| VOLUME SWELL : AT 70ºC FOR 72 HRS | ASTM D 471 | |||
| IN IRM OIL NO.1 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.2 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.3 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | FAIR | ASTM D 1149 | FAIR | |
| — DILUTE ACIDS AND BASES | FAIR | FAIR | ||
| — CONCENTRATED ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — OILS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — SOLVENTS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| TEMPERATURE RANGE | -25º TO + 70º C | -25º TO + 70º C | ||
| COLOUR | TAN – RAL 1013 | |||
| PROPERTIES | TEST METHOD | VALUES FPS UNITS | TEST METHOD | VALUES METRIC UNITS |
| SPECIFIC GRAVITY | DIN 53508 | 1.20 ±0.05 | ASTM D297 | 1.20 ±0.05 |
| HARDNESS | DIN 53505 | 45 ± 5 SH A | ASTM D2240 | 45 ± 5 SH A |
| TENSILE STRENGTH ( MIN ) | DIN 53504 | 1425 PSI | ASTM D412 | 100 KG/CM2 |
| ELONGATION AT BREAK ( MIN ) | DIN 53504 | 400% | ASTM D412 | 400% |
| ABRASION RESISTANCE ( MAX ) | DIN 53516 | 150 MM3 | ASTM D5963 | 150 MM3 |
| COMPRESSION SET (70ºC/24 HRS/25% COMPRESSION) (MAX) | DIN 53517 | 35% | ASTM D395 METHOD B | 35% |
| TEAR RESISTANCE ( ANGULAR ) MIN | DIN 53515 | 140 LBS/INCH | ASTM D624 | 25 KG/CM |
| CHANGE IN PROPERTIES AFTER | ||||
| HEAT AGEING FOR ( 72 HRS. AT 70 ºC ) | ASTM D573 | |||
| — HARDNESS (PTS) | + 5 (MAX) | + 5 (MAX) | ||
| — TENSILE STRENGTH (%) | + 10 / – 20 | + 10 / – 20 | ||
| — ELONGATION AT BREAK (%) | + 10 / – 20 | + 10 / – 20 | ||
| VOLUME SWELL : AT 70ºC FOR 72 HRS | ASTM D 471 | |||
| IN IRM OIL NO.1 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.2 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| IN IRM OIL NO.3 | NOT RECOMMENDED | NOT RECOMMENDED | ||
| CHEMICAL RESISTANCE | ||||
| — OZONE | FAIR | ASTM D 1149 | FAIR | |
| — DILUTE ACIDS AND BASES | FAIR | FAIR | ||
| — CONCENTRATED ACIDS AND BASES | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — OILS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| — SOLVENTS | NOT RECOMMENDED | NOT RECOMMENDED | ||
| TEMPERATURE RANGE | -25º TO + 70º C | -25º TO + 70º C | ||
| COLOUR | TAN – RAL 1013 | |||