Natural Rubber BS1154 Z60 Strip
- Certified to BS1154
- REACH, RoHS, PAH and CE compliant
- High Tensile and Abrasion resistance
- High Quality Natural Rubber: 60° Shore
- View material – Coru232
Call for Price
|
PROPERTIES |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
BS 903: PART A1 |
1.20 |
|
HARDNESS |
BS 903: PART A26 |
60 ± 5 IRHD |
|
TENSILE STRENGTH (KG/CM2) |
BS 903: PART A2 |
170 |
|
ELONGATION AT BREAK ( MIN ) |
BS 903: PART A2 |
400% |
|
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) |
BS 903: PART A6 |
30% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
BS 903: PART A3 |
50 KG/CM |
|
ABRASION RESISTANCE |
|
120mm3 |
|
CHANGE IN PROPERTIES |
|
|
|
HEAT AGEING (168 HRS. AT 70ºC ) |
BS 903: PART A 19 |
|
|
— HARDNESS (PTS) |
BS 903: PART A26 |
+ 5 / -5 (MAX) |
|
— TENSILE STRENGTH (%) |
BS 903: PART A2 |
-10 (MAX) |
|
— ELONGATION AT BREAK (%) |
BS 903: PART A2 |
-15 (MAX) |
|
POLYMER CONTENT (NATURAL RUBBER) |
|
100% |
|
ADDITIONAL INFORMATION – |
|
|
|
CHEMICAL RESISTANCE |
|
|
|
— OZONE |
BS 903: PART A43 |
GOOD |
|
— DILUTE ACIDS AND BASES |
BS 903: PART A16 |
FAIR |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-20º TO + 70ºC |
|
COLOUR |
|
BLACK |
|
PROPERTIES |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
BS 903: PART A1 |
1.20 |
|
HARDNESS |
BS 903: PART A26 |
60 ± 5 IRHD |
|
TENSILE STRENGTH (KG/CM2) |
BS 903: PART A2 |
170 |
|
ELONGATION AT BREAK ( MIN ) |
BS 903: PART A2 |
400% |
|
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) |
BS 903: PART A6 |
30% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
BS 903: PART A3 |
50 KG/CM |
|
ABRASION RESISTANCE |
|
120mm3 |
|
CHANGE IN PROPERTIES |
|
|
|
HEAT AGEING (168 HRS. AT 70ºC ) |
BS 903: PART A 19 |
|
|
— HARDNESS (PTS) |
BS 903: PART A26 |
+ 5 / -5 (MAX) |
|
— TENSILE STRENGTH (%) |
BS 903: PART A2 |
-10 (MAX) |
|
— ELONGATION AT BREAK (%) |
BS 903: PART A2 |
-15 (MAX) |
|
POLYMER CONTENT (NATURAL RUBBER) |
|
100% |
|
ADDITIONAL INFORMATION – |
|
|
|
CHEMICAL RESISTANCE |
|
|
|
— OZONE |
BS 903: PART A43 |
GOOD |
|
— DILUTE ACIDS AND BASES |
BS 903: PART A16 |
FAIR |
|
— CONCENTRATED ACIDS AND BASES |
|
NOT RECOMMENDED |
|
— OILS |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-20º TO + 70ºC |
|
COLOUR |
|
BLACK |