Flame Retardant UL94-VO EPDM Strip
- Flame Resistance to DIN75200 – UL94VO – Pass
- REACH, RoHS, PAH and CE compliant
- High Grade EPDM compound: 60º Shore
- View material – Coru176
Call for Price
Chemical Resistances
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
ASTM D297 |
1.40 ± 0.05 |
DIN 53508 |
1.40 ± 0.05 |
|
HARDNESS |
ASTM D2240 |
65 ± 5 SH A |
DIN 53505 |
65 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
ASTM D412 |
711 PSI |
DIN 53504 |
50 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
ASTM D412 |
200% |
DIN 53504 |
200% |
|
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
ASTM D395 METHOD B |
50% |
DIN 53517 |
50% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
ASTM D624 |
112 LBS/INCH |
DIN 53515 |
20 KG/CM |
|
ANTI STATIC CHARACTERISTIC |
ASTM D257 |
10⁴ to 10⁸ |
ASTM D257 |
10⁴ to 10⁸ |
|
CHANGE IN PROPERTIES |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 70ºC ) |
ASTM D573 |
|
|
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / – 10 |
|
+ 10 / – 10 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / – 20 |
|
+ 10 / – 20 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN |
ASTM D 471 |
|
|
|
|
ASTM OIL NO.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
ASTM OIL NO.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
ASTM OIL NO.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
FLAMMABILITY TEST |
UL94, V-O |
PASS |
UL94, V-O |
PASS |
|
LSOH (LOW SMOKE ZERO HALOGEN) |
|
PASS |
|
PASS |
|
POLYMER CONTENT (EPDM) |
|
100% |
|
100% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
ASTM D 1149 |
EXCELLENT |
|
EXCELLENT |
|
— DILUTE ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
— CONCENTRATED ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
— OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-30º TO + 130ºC |
|
-30º TO + 130ºC |
|
COLOUR |
|
BLACK |
||
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
ASTM D297 |
1.40 ± 0.05 |
DIN 53508 |
1.40 ± 0.05 |
|
HARDNESS |
ASTM D2240 |
65 ± 5 SH A |
DIN 53505 |
65 ± 5 SH A |
|
TENSILE STRENGTH ( MIN ) |
ASTM D412 |
711 PSI |
DIN 53504 |
50 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
ASTM D412 |
200% |
DIN 53504 |
200% |
|
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) |
ASTM D395 METHOD B |
50% |
DIN 53517 |
50% |
|
TEAR RESISTANCE ( ANGULAR ) MIN |
ASTM D624 |
112 LBS/INCH |
DIN 53515 |
20 KG/CM |
|
ANTI STATIC CHARACTERISTIC |
ASTM D257 |
10⁴ to 10⁸ |
ASTM D257 |
10⁴ to 10⁸ |
|
CHANGE IN PROPERTIES |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 70ºC ) |
ASTM D573 |
|
|
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+ 10 / – 10 |
|
+ 10 / – 10 |
|
— ELONGATION AT BREAK (%) |
|
+ 10 / – 20 |
|
+ 10 / – 20 |
|
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN |
ASTM D 471 |
|
|
|
|
ASTM OIL NO.1 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
ASTM OIL NO.2 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
ASTM OIL NO.3 |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
FLAMMABILITY TEST |
UL94, V-O |
PASS |
UL94, V-O |
PASS |
|
LSOH (LOW SMOKE ZERO HALOGEN) |
|
PASS |
|
PASS |
|
POLYMER CONTENT (EPDM) |
|
100% |
|
100% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
ASTM D 1149 |
EXCELLENT |
|
EXCELLENT |
|
— DILUTE ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
— CONCENTRATED ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
— OILS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
— SOLVENTS |
|
NOT RECOMMENDED |
|
NOT RECOMMENDED |
|
TEMPERATURE RANGE |
|
-30º TO + 130ºC |
|
-30º TO + 130ºC |
|
COLOUR |
|
BLACK |
||