SM149 is a genuine, Chemours Viton A Rubber at 70 Shore.
Genuine Chemours Viton sheeting refers to viton grades produced from authentic Viton compounds produced by Chemours. These sheets are designed to provide exceptional performance in challenging environments where resistance to harsh chemicals, extreme temperatures, and exposure to various fluids is crucial. Common applications for Viton sheeting include gaskets, seals, and other components in industries such as aerospace, automotive, chemical processing, and oil and gas.
Key features of genuine Chemours Viton sheeting may include:
- Chemical Resistance: Viton is known for its resistance to a wide range of chemicals, including oils, fuels, acids, and solvents.
- High Temperature Stability: Viton can withstand high temperatures, making it suitable for applications where other elastomers may degrade.
- Weather Resistance: Viton materials are often resistant to ozone, sunlight, and other environmental factors, ensuring long-term durability.
- Sealing Performance: The material’s excellent sealing properties make it a preferred choice for gaskets and seals in various industries.
- Versatility: Genuine Chemours Viton sheeting is versatile and can be used in diverse industrial settings, contributing to its widespread use.
When considering Viton sheeting for specific applications, it’s essential to verify the product’s authenticity and quality. Suppliers or distributors authorised by Chemours can provide assurance that the material being purchased is genuine and meets the required specifications.
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.95 ± 0.05 |
ASTM D297 |
1.95 ± 0.05 |
|
HARDNESS |
DIN 53505 |
70 ± 5 SH A |
ASTM D2240 |
70 ± 5 SH A |
|
TENSILE STRENGTH (min) |
DIN 53504 |
835 PSI |
ASTM D412 |
60 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
250% |
ASTM D412 |
250% |
|
COMPRESSION SET (150ºC/24 HRS/25% SET) (MAX) |
DIN 53517 |
35% |
ASTM D395 METHOD B |
35% |
|
TEAR RESISTANCE (Angular) Min |
DIN 53515 |
112 Lbs/Inch |
ASTM D264 |
20 Kg/cm |
|
ANTISTATIC CHARACTERISTIC |
ASTM D257 |
>10^3 |
ASTM D257 |
>10^3 |
|
POLYMER CONTENT (%) |
|
100 |
|
100 |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 150 ºC ) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+10 / -10 |
|
+ 15 |
|
— ELONGATION AT BREAK (%) |
|
+15 / -15 |
|
+25 / -25 |
|
VOLUME SWELL : AT 150ºC FOR 72 HRS/IN |
|
|
ASTM D 471 |
|
|
ASTM OIL NO 901 |
|
-6% |
|
-6% |
|
ASTM OIL NO 902 |
|
-1% |
|
-1% |
|
ASTM OIL NO 903 |
|
+5% |
|
+5% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
EXCELLENT |
ASTM D 1149 |
EXCELLENT |
|
— DILUTE ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
— CONCENTRATED ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
— OILS |
|
VERY GOOD |
|
VERY GOOD |
|
— SOLVENTS |
|
VERY GOOD |
|
VERY GOOD |
|
TEMPERATURE RANGE |
|
-30º TO + 275º C |
|
-30º TO + 275º C |
|
COLOUR |
|
BLACK |
||
|
PROPERTIES |
TEST METHOD |
VALUES FPS UNITS |
TEST METHOD |
VALUES METRIC UNITS |
|
SPECIFIC GRAVITY |
DIN 53508 |
1.95 ± 0.05 |
ASTM D297 |
1.95 ± 0.05 |
|
HARDNESS |
DIN 53505 |
70 ± 5 SH A |
ASTM D2240 |
70 ± 5 SH A |
|
TENSILE STRENGTH (min) |
DIN 53504 |
835 PSI |
ASTM D412 |
60 KG/CM2 |
|
ELONGATION AT BREAK ( MIN ) |
DIN 53504 |
250% |
ASTM D412 |
250% |
|
COMPRESSION SET (150ºC/24 HRS/25% SET) (MAX) |
DIN 53517 |
35% |
ASTM D395 METHOD B |
35% |
|
TEAR RESISTANCE (Angular) Min |
DIN 53515 |
112 Lbs/Inch |
ASTM D264 |
20 Kg/cm |
|
ANTISTATIC CHARACTERISTIC |
ASTM D257 |
>10^3 |
ASTM D257 |
>10^3 |
|
POLYMER CONTENT (%) |
|
100 |
|
100 |
|
CHANGE IN PROPERTIES AFTER |
|
|
|
|
|
HEAT AGEING ( 72 HRS. AT 150 ºC ) |
|
|
ASTM D573 |
|
|
— HARDNESS (PTS) |
|
+ 5 (MAX) |
|
+ 5 (MAX) |
|
— TENSILE STRENGTH (%) |
|
+10 / -10 |
|
+ 15 |
|
— ELONGATION AT BREAK (%) |
|
+15 / -15 |
|
+25 / -25 |
|
VOLUME SWELL : AT 150ºC FOR 72 HRS/IN |
|
|
ASTM D 471 |
|
|
ASTM OIL NO 901 |
|
-6% |
|
-6% |
|
ASTM OIL NO 902 |
|
-1% |
|
-1% |
|
ASTM OIL NO 903 |
|
+5% |
|
+5% |
|
CHEMICAL RESISTANCE |
|
|
|
|
|
— OZONE |
|
EXCELLENT |
ASTM D 1149 |
EXCELLENT |
|
— DILUTE ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
— CONCENTRATED ACIDS AND BASES |
|
EXCELLENT |
|
EXCELLENT |
|
— OILS |
|
VERY GOOD |
|
VERY GOOD |
|
— SOLVENTS |
|
VERY GOOD |
|
VERY GOOD |
|
TEMPERATURE RANGE |
|
-30º TO + 275º C |
|
-30º TO + 275º C |
|
COLOUR |
|
BLACK |
||