Free delivery on orders over £1200.00, all other orders have a fixed rate of £20.00 + VAT.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
*Terms and conditions apply
If you would like to discuss this product, or you require a sample, please call 01702 560194. Alternatively, you can use our contact form.
Please note: All cut material is non-returnable unless faulty as these are non-sellable and have been cut to specific requirements.
3 PLY 7mm thick EP315/3
SKU: EP315/3-Din-Y-conveyor-belting
- 3 Ply Belt
- 7mm Thick
- 315N/mm Tensile Strength
- Manufactured to DIN Y
- No minimum or maximum length
Call for Price
3 Ply EP315/3 – 3 + 1.5 DIN Y Conveyor belting from Coruba has 3 Polyester Fabric Reinforcements with a tensile strength of 315 N/mm. This belt has a 3mm hard wearing rubber top and a 1.5mm Bottom cover, manufactured to International standard DIN Y.
Available in the following widths: 1.5m, 1.2m, 0.75m, 0.6m
Technical Information
|
PROPERTIES |
VALUES |
| Carcass | |
| The carcass is built up of 2 fabrics of polyester warp and polyamide weft: | |
| Tensile Strength for 50 x 200mm Longitudinal, kgf Min Tranversal kgf Min |
2000 400 |
| Adhesion between plies [N/mm]: | 5 |
| Thickness [mm]: | 2.2 |
| Elongation at 10% TS nom [&]: | MAX 1.5 |
| Covers: | |
| Top cover thickness [mm]: | 3 |
| Heat resistant, anti-static as per ISO284, SBR: | |
| Bottom cover thickness [mm]: | 1.5 |
| Minimum adhesion between cover and carcass [N/mm]: | 5 |
| Top: | 5 |
| Bottom: | 4.5 |
| Technical data of rubber covers DIN Y | |
| Tensile strength in accordance to SR ISO 37 | 200 kgf/cm² |
| Elongation at break [%]: to SR ISO 37 | 400% |
| Abrasion resistance [mm³]: | 150 |
| Ozone resistance ( 50 pphm: elongation 15%/ 72 hrs / 40°C +/- 2°C) |
No Cracks |
| Surface electrical resistance in accordance with SR EN ISO 284 Ώ, max |
3 x 10⁸ |
| Resistance to accelerated ageing (168hr @ 70°C) in accordance with ISO 1880 -Change of Tensile Strength – Decrease of elongation at break |
+/- 25% |
| Max abrasion resistance [mm³]: | 150 |
| Hardness, ±5º [ºShore A]: | 65±5 |
|
PROPERTIES |
VALUES |
| Carcass | |
| The carcass is built up of 2 fabrics of polyester warp and polyamide weft: | |
| Tensile Strength for 50 x 200mm Longitudinal, kgf Min Tranversal kgf Min |
2000 400 |
| Adhesion between plies [N/mm]: | 5 |
| Thickness [mm]: | 2.2 |
| Elongation at 10% TS nom [&]: | MAX 1.5 |
| Covers: | |
| Top cover thickness [mm]: | 3 |
| Heat resistant, anti-static as per ISO284, SBR: | |
| Bottom cover thickness [mm]: | 1.5 |
| Minimum adhesion between cover and carcass [N/mm]: | 5 |
| Top: | 5 |
| Bottom: | 4.5 |
| Technical data of rubber covers DIN Y | |
| Tensile strength in accordance to SR ISO 37 | 200 kgf/cm² |
| Elongation at break [%]: to SR ISO 37 | 400% |
| Abrasion resistance [mm³]: | 150 |
| Ozone resistance ( 50 pphm: elongation 15%/ 72 hrs / 40°C +/- 2°C) |
No Cracks |
| Surface electrical resistance in accordance with SR EN ISO 284 Ώ, max |
3 x 10⁸ |
| Resistance to accelerated ageing (168hr @ 70°C) in accordance with ISO 1880 -Change of Tensile Strength – Decrease of elongation at break |
+/- 25% |
| Max abrasion resistance [mm³]: | 150 |
| Hardness, ±5º [ºShore A]: | 65±5 |